Erosion mechanisms during abrasive waterjet machining: model microstructures and single particle experiments

Mieszala, M. and Lozano Torrubia, Pablo and Axinte, Dragos A. and Schwiedrzik, J.J. and Mischler, S. and Michler, J. (2017) Erosion mechanisms during abrasive waterjet machining: model microstructures and single particle experiments. Journal of Materials Processing Technology, 247 . pp. 92-102. ISSN 0924-0136

[img] PDF - Repository staff only until 8 April 2019. - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader
Available under Licence Creative Commons Attribution Non-commercial No Derivatives.
Download (18MB)

Abstract

The erosion mechanisms during abrasive waterjet (AWJ) machining have been examined for a variety of materials. However, no systematic study has considered the effect of the microstructure–property relationship on the erosion mechanisms in metals. In this work, the influence of microstructure and mechanical properties on the erosion mechanisms is investigated using AWJ controlled-depth milling and single particle impact experiments performed on nanocrystalline, microcrystalline and single crystal nickel samples. The resulting footprints and subsurface microstructure evolution were analysed using advanced characterization techniques. The erosion rate of the target metal is found to correlate positively with grain size and negatively with hardness but this correlation is nonlinear. The subsurface microstructure of the single crystal and microcrystalline are altered, while only the texture of the nanocrystalline nickel is modified. The grain refinement mechanism observed in microcrystalline and single crystal microstructure is elucidated by electron backscatter diffraction. It proceeds by the generation of dislocations under severe plastic deformation, which transforms into subgrains before forming new grains under further strain. Therefore, severe plastic deformation induced by AWJ machining leads to surface nanocrystallization and induces substantial subsurface work-hardening, as revealed by nanoindentation tests and confirmed by single particle impacts, with the consequence that the erosion rate decreases with decreasing grain size. This work clarifies the erosion mechanisms in pure metals and highlights the dynamic nature of AWJ machining as a result of the complex interplay between microstructure, mechanical properties and material removal mechanisms, providing new insights into AWJ controlled-depth milling technique.

Item Type: Article
Keywords: Abrasive waterjet milling; Electroplating; Microstructure; Plasticity; Nickel; Nanoindentation
Schools/Departments: University of Nottingham, UK > Faculty of Engineering > Department of Mechanical, Materials and Manufacturing Engineering
Identification Number: 10.1016/j.jmatprotec.2017.04.003
Depositing User: Eprints, Support
Date Deposited: 27 Apr 2017 09:57
Last Modified: 28 Apr 2017 12:39
URI: http://eprints.nottingham.ac.uk/id/eprint/42353

Actions (Archive Staff Only)

Edit View Edit View